Refractory Industry
12mm, 20mm, 25mm, 35mm
1400- 1450
152 MPa
Chemical Composition (maximum unless stated): C Si Mn P S Cr Ni 0.25 1.5 1.5 0.030 0.030 24.0-27.0 19.0-22.0 | others - |
Melting Temperature: | 1400- 1450°C |
Critical Oxidation Temperature: Cyclic Heating: Continuous Service: | 1040 °C 1200 °C |
Tensile Strength: 20 °C 870 °C | 540 MPa 152 MPa |
Modulus of Elasticity (870ºC): | 125 GPa |
Coefficient of Thermal Expansion (870ºC): | 18.5 @10-6 /ºC |
Thermal Conductivity (540ºC): | 20.1 W/m2K |
Fiber Length *1 | Typical Equivalent Dia*2 | Typical Aspect Ratio *3 | Typical No/kg |
12mm | 0 .34mm | 40 | 151,000 |
20mm | 0.47mm | 50 | 51,000 |
25mm | 0.50mm | 50 | 26,000 |
25mm | 0 60mm | 42 | 18,100 |
35mm | 0.60mm | 58 | 13,000 |
35mm | 0.70mm | 50 | 9,500 |
PLS FEEL FREE TO CONTACT US:
Ms. Helen Chu
Mobile & WhatsApp: +86 18668055321
Skype: helenyuan413; QQ: 413367414
E-mail: helen(AT)elite-indus.com
Chemical Composition (maximum unless stated): C Si Mn P S Cr Ni 0.25 1.5 1.5 0.030 0.030 24.0-27.0 19.0-22.0 | others - |
Melting Temperature: | 1400- 1450°C |
Critical Oxidation Temperature: Cyclic Heating: Continuous Service: | 1040 °C 1200 °C |
Tensile Strength: 20 °C 870 °C | 540 MPa 152 MPa |
Modulus of Elasticity (870ºC): | 125 GPa |
Coefficient of Thermal Expansion (870ºC): | 18.5 @10-6 /ºC |
Thermal Conductivity (540ºC): | 20.1 W/m2K |
Fiber Length *1 | Typical Equivalent Dia*2 | Typical Aspect Ratio *3 | Typical No/kg |
12mm | 0 .34mm | 40 | 151,000 |
20mm | 0.47mm | 50 | 51,000 |
25mm | 0.50mm | 50 | 26,000 |
25mm | 0 60mm | 42 | 18,100 |
35mm | 0.60mm | 58 | 13,000 |
35mm | 0.70mm | 50 | 9,500 |