Copolymer Polypropylene Macro Synthetic Fiber Twist hybrid

ELT-TWIST is a 100% virgin blended copolymer synthetic Structural macro-fiber successfully used as an alternate to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications.

Quantity:



Inquire Add to Basket

Model:
ELT-TWIST
Brand:
ELITE-INDUS
Code:
5503400000
Material:
Copolymer Polypropylene
Tensile Strength:
500 to 800 Mpa
Elastic Modulas:
5000Mpa
Equivalent Diameter:
0.3mm+/-0.05mm
Density(g/cm3):
0.91+/-0.01 g/cm3
Melting Point(C Deg.):
160 - 170
Crack Elongation:
15+/-5%
Acid &Alkali Resistance:
Strong
Color:
White, Black, Gray,Natural

Product Description

Macro Synthetic Fiber TWIST hybrid

Description
ELT-TWIST is a 100% virgin blended copolymer synthetic Structural macro-fiber successfully used as an alternate to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications.

ELT-Twist is actually a Hybrid of two fibers: A standard fibrillated polypropylene fiber to reduce and control shrinkage and temperature cracking.
A twisted-bundle monofilament fiber made of a strong synthetic copolymer, to increase load-transfer and post-crack performance.

ELT-TWIST fibers comply with ASTM C1116, Standard Specification for Fiber Reinforced Concrete and Shotcrete, and are specifically used for the reduction of plastic shrinkage cracks, to improve impact, shatter and abrasion resistance, to increase fatigue resistance, to increase toughness of concrete and provide long term durability of concrete, structural enhancements and cement based building products.

Functions
· Increases impact, shatter and abrasion resistance of concrete
· Reduces segregation, plastic settlement, and shrinkage cracking of concrete
· Provides three-dimensional reinforcement against macro-cracking
· Increases overall durability, fatigue resistance and flexural toughness
· Reduction of in-place cost versus wire mesh for temperature / shrinkage crack control
· Easily added to concrete mixture at any time prior to placement

Application
· Industrial and residential floors
· Whitetoppings, bridge decks and pavements
· Thin walled pre-cast (septic tanks, vaults, walls, etc.)
· Mass concrete

Specification

*Density(g/cm 3 )*	0.91 +/- 0.01	*Equivalent Dia(mm)*	0.3±0.05
*Shape*	twist	*break tensile Ratio(%)*	8-15
*Crack Ratio* *(%)*	20+/-5	*Melting point ( C. Deg)*	160-170
*Tensile Strength* *(Mpa)*	500 to 800	*Water Absorption*	Negligible
*Elastic Modulus (*Mpa)	>3500	*Resistance to acid & alkali*	Excellent
*Material*	Virgin Copolymer/Polypropylene
*Length(mm)*	38/48 /54 or as per your request
Dosage rates will vary depending upon the reinforcing requirements and can range from 2kg/m³ to 5 kg/m³

Directions for Use

ELT-TWIST fibers can be added to the concrete mixture at any time prior to placement of the concrete.
It is generally recommended to add any fiber material at the ready-mix concrete plant during batching.

Fibers must be mixed with concrete for a minimum of three to five minutes at maximum mixing speed, depending on the mixer type, to ensure complete dispersion and uniformity.

Packing

*Shape*	*Inner Packing(PE* Film Bag)	*Outer Packing(Plastic Woven* Bag)	*20’gp*	*40’HQ*
*Twist*	0.5/1.0kg	10kg	5500kg	12000kg
	*Inner Packing(*Water Soluble Paper Bag)	*Outer Packing (Carton)*
	0.5/1.0kg	10kg	4000kg	9000kg
Other Packing Can As Per Your Request