Quantity: | |
---|---|
elite-indus
3206111000
below 400g
1000KGS by LCL
yes
Anatase grade, Nano grade
Index | Standard | |||||
| ELT-R2219 | ELT-R2198 | ELT-R2196 | ELT-R2178 | ELT-RM1 | |
Process | Rutile paint produced by sulfate process | |||||
Surface treatment | Treat with zirconium, aluminum silicon etc., | Treat with zirconium, silicon, aluminum, silicon etc., Special organic substance covering | Treat with aluminum etc, Special organic substance covering | Treat with Si, Al, Special organic substance covering | Treat with aluminum etc, Special organic substance covering | |
Standard classification (ISO 591-1) | R2 | |||||
Specific gravity (ISO787-10) | ---- | 4.0g/cm3 | 4.0g/cm3 | 3.9g/cm3 | --- | |
TIO2content (ISO591-1) | ≥92.5% | 92.0﹪min | 93.5% min. | ≥92.0﹪ | ≥90.0﹪ | |
105℃ volatile under package(ISO 787-2) | ≤0.5% | 0.5﹪max | 0.5% max. | ≤0.5﹪ | ≤0.5﹪ | |
Residue on sieve (45um)(ISO 787-18) | ≤0.01% | 0.01﹪max | 0.05% max. | ---- | ≤0.05﹪ | |
Rutile transformation rate | ≥99% | 99﹪min | 98% min. | ≥97﹪ | ≥97﹪ | |
Whiteness of oil systerm (L ﹡)note.1 | 95.0-95.5 | 94.7-95.5 | 93.5-95.0 | 94.5-95.0 | ||
PH Value of aqueous Suspension(ISO 787-9) | 6.5-8.0 | 7.0-8.5 | ||||
Oil Absorption volume ISO 787-5 | ≤20g/100g max | 21g/100gmax. | 20g/100g max. | |||
Resistivity of aqueous extract ISO 787-14 | ≥80Ω·M | ≥80Ω·M | ≥150Ω·M | | 50Ω·M max. | |
TCS value | ---- | ---- | --- | 1900min. | --- |
Index | Standard | |||||
| ELT-R2219 | ELT-R2198 | ELT-R2196 | ELT-R2178 | ELT-RM1 | |
Process | Rutile paint produced by sulfate process | |||||
Surface treatment | Treat with zirconium, aluminum silicon etc., | Treat with zirconium, silicon, aluminum, silicon etc., Special organic substance covering | Treat with aluminum etc, Special organic substance covering | Treat with Si, Al, Special organic substance covering | Treat with aluminum etc, Special organic substance covering | |
Standard classification (ISO 591-1) | R2 | |||||
Specific gravity (ISO787-10) | ---- | 4.0g/cm3 | 4.0g/cm3 | 3.9g/cm3 | --- | |
TIO2content (ISO591-1) | ≥92.5% | 92.0﹪min | 93.5% min. | ≥92.0﹪ | ≥90.0﹪ | |
105℃ volatile under package(ISO 787-2) | ≤0.5% | 0.5﹪max | 0.5% max. | ≤0.5﹪ | ≤0.5﹪ | |
Residue on sieve (45um)(ISO 787-18) | ≤0.01% | 0.01﹪max | 0.05% max. | ---- | ≤0.05﹪ | |
Rutile transformation rate | ≥99% | 99﹪min | 98% min. | ≥97﹪ | ≥97﹪ | |
Whiteness of oil systerm (L ﹡)note.1 | 95.0-95.5 | 94.7-95.5 | 93.5-95.0 | 94.5-95.0 | ||
PH Value of aqueous Suspension(ISO 787-9) | 6.5-8.0 | 7.0-8.5 | ||||
Oil Absorption volume ISO 787-5 | ≤20g/100g max | 21g/100gmax. | 20g/100g max. | |||
Resistivity of aqueous extract ISO 787-14 | ≥80Ω·M | ≥80Ω·M | ≥150Ω·M | | 50Ω·M max. | |
TCS value | ---- | ---- | --- | 1900min. | --- |