Quantity: | |
---|---|
Elt-Membrane
EltMembrane-TSHG
HDPE Geomembrane
HDPE Pond Liner/HDPE Liner
Black
1M to 8M, normal is 5.8M
Normal is 50M/100M or as per your request
HDPE Resin
ASTM D
CE
ISO
Waterproof
No. | Properties | Test Method | Test Value | ||||||
1 | Thickness(mm) | ASTM D5199 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
| 10mm min thickness measurement should be more than 8 | ASTM D5994 | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% |
2 | Rough surface height mm Note(1) | GM12 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 |
3 | Density (g/cm2) | ASTM D1505 | 0.94 | ||||||
4 | Tensile Propeties | | | ||||||
5 | Yield Strength(N/mm) | ASTM D6693 | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
6 | Break Strength(N/mm) | 8 | 10 | 13 | 16 | 21 | 26 | 32 | |
7 | Yield Elongation % | Type IV | 12 | ||||||
8 | Break Elongation % | 100 | |||||||
9 | Tear Resistance/N | ASTM D1004 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
10 | Puncture Resistance Strength/N | ASTM D4833 | 200 | 267 | 333 | 400 | 534 | 667 | 800 |
11 | Stress Crack resistance/hr | ASTM D5397 (App.) | 300 | ||||||
| Carbon Black | | |||||||
12 | Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||
13 | Carbon Black Dispersion | ASTM D5596 | 10 9viewing area should fall in the first grade or second grade, third grade is not more than 1 | ||||||
14 | Oxidative Induction Time(OIT) | | |||||||
Standard OIT/min | ASTM D3895 | 100 | |||||||
High Pressure OIT/min | ASTM D5885 | 400 | |||||||
15 | Oven Aging at 85°C | | |||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | |||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | |||||||
16 | UV Resistance | | |||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | |||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | |||||||
17 | Note(1)in 10 tests,the results of which should be more than 8 times 0.18mm,the min should be greater than 0.13mm.Rough surface on the double gemembrane should be measured alternately in the two sides. |
No. | Properties | Test Method | Test Value | ||||||
1 | Thickness(mm) | ASTM D5199 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
| 10mm min thickness measurement should be more than 8 | ASTM D5994 | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% | -5% -10% -15% |
2 | Rough surface height mm Note(1) | GM12 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 | 0.25 |
3 | Density (g/cm2) | ASTM D1505 | 0.94 | ||||||
4 | Tensile Propeties | | | ||||||
5 | Yield Strength(N/mm) | ASTM D6693 | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
6 | Break Strength(N/mm) | 8 | 10 | 13 | 16 | 21 | 26 | 32 | |
7 | Yield Elongation % | Type IV | 12 | ||||||
8 | Break Elongation % | 100 | |||||||
9 | Tear Resistance/N | ASTM D1004 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
10 | Puncture Resistance Strength/N | ASTM D4833 | 200 | 267 | 333 | 400 | 534 | 667 | 800 |
11 | Stress Crack resistance/hr | ASTM D5397 (App.) | 300 | ||||||
| Carbon Black | | |||||||
12 | Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||
13 | Carbon Black Dispersion | ASTM D5596 | 10 9viewing area should fall in the first grade or second grade, third grade is not more than 1 | ||||||
14 | Oxidative Induction Time(OIT) | | |||||||
Standard OIT/min | ASTM D3895 | 100 | |||||||
High Pressure OIT/min | ASTM D5885 | 400 | |||||||
15 | Oven Aging at 85°C | | |||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | |||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | |||||||
16 | UV Resistance | | |||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | |||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | |||||||
17 | Note(1)in 10 tests,the results of which should be more than 8 times 0.18mm,the min should be greater than 0.13mm.Rough surface on the double gemembrane should be measured alternately in the two sides. |