Quantity: | |
---|---|
Elt-Membrane
EltMembrane-SSHG
HDPE Geomembrane
HDPE Pond Liner/HDPE Liner
Black
1M to 8M, normal is 5.8M
Normal is 50M/100M or as per your request
HDPE Resin
ASTM D
CE
ISO
Waterproof
No. | Properties | Test Method | Test Value | |||||||
1 | Thickness(mm) | ASTM D5199 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
2 | Density (g/cm2) | ASTM D1505 | 0.939 | |||||||
3 | Tensile Propeties | | | |||||||
Yield Strength(N/mm) | ASTM D6693 | 7 | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
Break Strength(N/mm) | 13 | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
Yield Elongation % | Type IV | 12 | ||||||||
Break Elongation % | 700 | |||||||||
4 | Tear Resistance/N | ASTM D1004 | 62 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
5 | Puncture Resistance/N | ASTM D4833 | 160 | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
6 | Stress Crack resistance/hr | ASTM D5397 (App.) | 300 | |||||||
7 | Carbon Black | | ||||||||
Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||||
Carbon Black Dispersion | ASTM D5596 | Carbon black dispersion(only near spherical agglomerates)for 10 different views 9 in categories 1 or 2 and 1 in category 3 | ||||||||
8 | Oxidative Induction Time(OIT) | | ||||||||
Standard OIT/min | ASTM D3895 | 100 | ||||||||
High Pressure OIT/min | ASTM D5885 | 400 | ||||||||
9 | Oven Aging at 85°C | | ||||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | ||||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | ||||||||
10 | UV Resistance | | ||||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | ||||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | ||||||||
11 | Low tempreture impact brittle property at -70°C | _ | Pass | |||||||
12 | Permeability g·cm/(cm2)·Pa | _ | ≤1.0×10-13 | |||||||
13 | Dimensional Stability/% | _ | ±2 |
No. | Properties | Test Method | Test Value | |||||||
1 | Thickness(mm) | ASTM D5199 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
2 | Density (g/cm2) | ASTM D1505 | 0.939 | |||||||
3 | Tensile Propeties | | | |||||||
Yield Strength(N/mm) | ASTM D6693 | 7 | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
Break Strength(N/mm) | 13 | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
Yield Elongation % | Type IV | 12 | ||||||||
Break Elongation % | 700 | |||||||||
4 | Tear Resistance/N | ASTM D1004 | 62 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
5 | Puncture Resistance/N | ASTM D4833 | 160 | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
6 | Stress Crack resistance/hr | ASTM D5397 (App.) | 300 | |||||||
7 | Carbon Black | | ||||||||
Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||||
Carbon Black Dispersion | ASTM D5596 | Carbon black dispersion(only near spherical agglomerates)for 10 different views 9 in categories 1 or 2 and 1 in category 3 | ||||||||
8 | Oxidative Induction Time(OIT) | | ||||||||
Standard OIT/min | ASTM D3895 | 100 | ||||||||
High Pressure OIT/min | ASTM D5885 | 400 | ||||||||
9 | Oven Aging at 85°C | | ||||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | ||||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | ||||||||
10 | UV Resistance | | ||||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | ||||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | ||||||||
11 | Low tempreture impact brittle property at -70°C | _ | Pass | |||||||
12 | Permeability g·cm/(cm2)·Pa | _ | ≤1.0×10-13 | |||||||
13 | Dimensional Stability/% | _ | ±2 |