HDPE Anti-skid Point Geomembrane

EltMembrane-APHG series of geomembrane is produced by processing of hot-welt, extrude, press pre-long. extension in reasonable controlling, which increase products' tensile strength puncture strength, abrasion resistance.

Quantity:
  • Elt-Membrane
  • EltMembrane-APHG
  • HDPE Geomembrane
  • HDPE Pond Liner/HDPE Liner
  • Black
  • 1M to 6M, normal is 5.8M
  • Normal is 50M/100M or as per your request
  • HDPE Resin
  • ASTM D
  • CE
  • ISO
  • Waterproof
HDPE Anti-skid Point Geomembrane
                         --------EltMembrane-APHG
Introduction:
 
EltMembrane-APHG series of geomembrane is produced by processing of hot-welt, extrude, press pre-long. extension in reasonable controlling, which increase products' tensile strength puncture strength, abrasion resistance.
 
The Points evenly distributed with increased friction, and the appearance is very beautiful. The two sides of geomembrane can be of melted together by different colour and materials.
We can produce right side or reverse of products according to geological conditions and project requirements. 
 
It retains suprior mechanical property and excellent elongation and stable chemical property of raw materials. And through adding functional auxiliaries agents in fixed proportion, which improved product's function of anti-acid&alkali and anti-corrosion. It's tensile strength 3 times higher than normal 1 textured geomembrane.
 
Features: 
 
1,High friction, 
2,anti-seepage, 
3,anti-pollution, anti-skid function, 
4,easy for construction.
 
Application:
 
Typical application ideal materials in landfill, anti-seepage and anti-fouling project for separation, waterproofing and anti-pollution.
 
 
 
 
 
Technical Specification:(CJ/T234-2006)(USA GRI-GM13 Standards)
No Value(mm) Text Value
0.75 1.00 1.25 1.50 2.00 2.50 3.00
1 Density (g/cm2)   0.939
2 Tensile Propeties
Yield Strength(N/mm) 11 15 18 22 29 37 44
Break Strength(N/mm) 8 10 13 16 21 26 32
Yield Elongation % 12
Break Elongation %  100
3 Tear Resistance/N 93 125 156 187 249 311 374
4 Puncture Resistance/N 200 267 333 400 534 667 800
5 Stress Crack Tesistance/h 300
6 Carbon Black 
Carbon Black Content % 2.0-3.0
Carbon Black Dispersion Note(1)
7 Oxidative Induction Time(OIT)
Standard OIT/min 100
High Pressure OIT/min 400
8 Oven Aging at 85°C
Standard OIT-% retained after 90 days 55
High pressure OIT-% retained after 90 days 80
9 UV Resistance
Standard OIT retained after 1600 hrs Not recommended since the high temperature of the Std-OIT test produces an unrealistic result for some of the antioxidants in the UV exposed samples
High pressure OIT retained after 1600 hrs 50
10 Low tempreture impact brittle property at -70°C Pass
11 Permeability g·cm/(cm2)·Pa 1.0×10-13
12 Dimensional Stability/% ±2
 
Note(1)Carbon black dispersion(only near spherical agglomerates)for 10 different views 9 in categorise 1 or 2 and 1 in category 
 
      

CONTACT US

Add: 18F Tower C, Winning Ocean Plaza, No. 680 South Maanshan Road, Hefei, China
Tel: 0086-551-6237 2118       
Fax: 0086-551-6237 2117

SALES

Tel: 0086-551-6237 2126, 6237 2128
       E-mail: Jackhu@elite-indus.com
Complain & Suggestions: 
       Tel: 0086-551-6237 2125
       Email: admin@elite-indus.com

Anhui Elite Industrial Co.,ltd

Copyright © 2015,Anhui Elite Industrial Co.,ltd