ELT-40/43
elite-indus
390440
Vinyl polymer resin
Vinyl Chloride and Vinyl Acetate Copolymers Resins ELT-40/43
Description:
ELT 40/43: It is special-modified vinyl resin as exclusive use for application UV inks and offers a desirable balance of chemical resistance、excellent ester soluble、good solubility property in UV monomer、film-forming、solvent release、paint film strength and thermoplasticity etc, which has excellent interbedded adhesion and good bridging function.In UV system, it can provide good dispersibility in pigment、improve the flexibility and plumpness of paint film and adhesive force of material base、 lessen the procedure of base coating, and it can reach VOC zero release and conform to the requirements of environmental protection;
It also has well sealing property in low temperature due to its lower melt index. It can be best soluble in HDDA、TMPTA etc monomer in UV system with resin solution 10-20% solid content, and it can also be dissolved in part of solvent and part of monomer to get higher solid content.
Specifications:
Items | Standard | Test method |
Appearance | White powder | By visual |
Whiteness | ≥80 | GB2913-82 |
Composition % by Wt | Vinyl Chloride 60±2% | GB/T7139-2002 |
Vinyl Acetate 40±2% | ISO1159- 1978 | |
K Value | 42 | GB/T 3401- 1999 |
Viscosity No. ml/g | 43±3 | GB/T 3401- 1999 |
Glass Transition Temp C | About 58 | GB11998-89 |
Average Molecular Wt | About 30000 | Calculated by the Viscosity No. |
% by wt, through 60 mesh | 100% | GB/T6003 1 |
Apparent density (g/ml) | ≥0.5 | GB20022-2005 |
Volatilization (%) | ≤1% | GB/T2914- 1999 |
Impurity Particle No. / 100g | ≤20 | GB9348-88 |
Solubility (25% EA solution) | Colorless and Transparent | By visual |
Potential Applications:
1. UV varnish: solution colorless transparent, high gloss of paint film .
2. UV ink: the pigment has a good wettability, improve the pigment development.
3. UV coating: provides adhesion to the substrate (PVC, PU,paper, PC, etc.), provides excellent flexibility and high bending resistance.
4. PTP aluminum foil heat sealing adhesive: it is used in combination with carboxyl vinyl resin to greatly reduce heat sealing temperature ( 150C to 140C) and improve heat sealing strength on aluminum and PVC heat sealing.
5. All-in-one machine paper adhesive: improve the adhesion fastness to the paper.
6. Hot stamping coating: reduce the stamping temperature and provide adhesion to the substrate.
7.Carbon belt: reduce melting temperature and provide adhesion.
Solubility:
1. In the UV system, it can be well dissolved in HDDA, TMPTA or cationic monomers to make a resin solution of 10-40% solids, and can also dissolve part of solvents and part of monomers to achieve a higher Solid, colorless and transparent solution.
2. The solid content of the ester solvent is recommended to be 20% -25%, the solvent is recommended: EA,NPAC, NBAC, etc., the solution is colorless and transparent.
3. The solid content of ketone solvent is recommended to be 20% -30%, the solvent is recommended: MEK, MIBK, CYC, etc., the solution is colorless and transparent.
Packing & storage:
1, 25kgs/ kraft bag, about 15000kgs /1x20’GP with pallet.
2, Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and
caution against wet. Must be transported in clean vehicle with awning and keep away from moisture.
It is NOT hazardous article, and the shelf life is one year from the production date.
Vinyl polymer resin
Vinyl Chloride and Vinyl Acetate Copolymers Resins ELT-40/43
Description:
ELT 40/43: It is special-modified vinyl resin as exclusive use for application UV inks and offers a desirable balance of chemical resistance、excellent ester soluble、good solubility property in UV monomer、film-forming、solvent release、paint film strength and thermoplasticity etc, which has excellent interbedded adhesion and good bridging function.In UV system, it can provide good dispersibility in pigment、improve the flexibility and plumpness of paint film and adhesive force of material base、 lessen the procedure of base coating, and it can reach VOC zero release and conform to the requirements of environmental protection;
It also has well sealing property in low temperature due to its lower melt index. It can be best soluble in HDDA、TMPTA etc monomer in UV system with resin solution 10-20% solid content, and it can also be dissolved in part of solvent and part of monomer to get higher solid content.
Specifications:
Items | Standard | Test method |
Appearance | White powder | By visual |
Whiteness | ≥80 | GB2913-82 |
Composition % by Wt | Vinyl Chloride 60±2% | GB/T7139-2002 |
Vinyl Acetate 40±2% | ISO1159- 1978 | |
K Value | 42 | GB/T 3401- 1999 |
Viscosity No. ml/g | 43±3 | GB/T 3401- 1999 |
Glass Transition Temp C | About 58 | GB11998-89 |
Average Molecular Wt | About 30000 | Calculated by the Viscosity No. |
% by wt, through 60 mesh | 100% | GB/T6003 1 |
Apparent density (g/ml) | ≥0.5 | GB20022-2005 |
Volatilization (%) | ≤1% | GB/T2914- 1999 |
Impurity Particle No. / 100g | ≤20 | GB9348-88 |
Solubility (25% EA solution) | Colorless and Transparent | By visual |
Potential Applications:
1. UV varnish: solution colorless transparent, high gloss of paint film .
2. UV ink: the pigment has a good wettability, improve the pigment development.
3. UV coating: provides adhesion to the substrate (PVC, PU,paper, PC, etc.), provides excellent flexibility and high bending resistance.
4. PTP aluminum foil heat sealing adhesive: it is used in combination with carboxyl vinyl resin to greatly reduce heat sealing temperature ( 150C to 140C) and improve heat sealing strength on aluminum and PVC heat sealing.
5. All-in-one machine paper adhesive: improve the adhesion fastness to the paper.
6. Hot stamping coating: reduce the stamping temperature and provide adhesion to the substrate.
7.Carbon belt: reduce melting temperature and provide adhesion.
Solubility:
1. In the UV system, it can be well dissolved in HDDA, TMPTA or cationic monomers to make a resin solution of 10-40% solids, and can also dissolve part of solvents and part of monomers to achieve a higher Solid, colorless and transparent solution.
2. The solid content of the ester solvent is recommended to be 20% -25%, the solvent is recommended: EA,NPAC, NBAC, etc., the solution is colorless and transparent.
3. The solid content of ketone solvent is recommended to be 20% -30%, the solvent is recommended: MEK, MIBK, CYC, etc., the solution is colorless and transparent.
Packing & storage:
1, 25kgs/ kraft bag, about 15000kgs /1x20’GP with pallet.
2, Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and
caution against wet. Must be transported in clean vehicle with awning and keep away from moisture.
It is NOT hazardous article, and the shelf life is one year from the production date.