Vinyl Copolymer resin for printing inks (screen & gravure)
Vinyl polymer resin
Specification:
1. Vinyl Copolymer resin (CAS NO.:9003-22-9)
It is a White powder, mainly use for Printing inks (screen & gravure),
Adhesive for PVC, heat-seal lacquer, Coating for leather & plastic etc.....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a) mPa.s | |
VC | VAC | ||||
VC50A | 85.0±1.0 | 15.0±1.0 | 52±1 | 75 | 43±10 |
VC55A | 87.0±1.0 | 13.0±1.0 | 55±1 | 76 | 52±10 |
VC62A | 87.0±1.0 | 13.0±1.0 | 62±1 | 76 | 75±10 |
VC68A | 87.0±1.0 | 13.0±1.0 | 68±1 | 76 | 90±20 |
2. Carboxyl Modified Vinyl Terpolymer Resin (CAS NO.:9005-09-8)
It is a White powder,mainly use for Screen printing ink, Gravure ink,
Adhesive for Aluminum foil heat-seal lacquer, Coating & Paint etc....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a) mPa.s | Acid value | ||
VC | VAc | Other(b) | |||||
VCVAM | 84.0±1.0 | 15±1.0 | 1.0 | 55±1 | 74 | 49±10 | 7.0±1.5 |
VCVAA | 85.0±1.0 | 14±1.0 | 1.0 | 61±1 | 75 | 65±10 | 7.0±1.5 |
VCVAB | 85.0±1.0 | 14±1.0 | 1.0 | 55±1 | 75 | 60±10 | 7.0±1.5 |
VCVAC | 84.0±1.0 | 14±1.0 | 2.0 | 55±1 | 73 | 60±10 | 14.0±2.0 |
3. Hydroxyl Modified Vinyl Terpolymer Resin (CAS NO.:25086-48-0)
Mainly use for PET Lamination ink, gravure & flexo printing ink,
Adhesive for tape& magnetic, Coating & Paint etc....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a1) mPa.s | Whiteness | ||
VC | VAc | Other(c) | |||||
VCOH | 88.0±1.0 | 6.0±1.0 | 6.0 | 61±2 | 76 | 240±20 | 60 |
VCH | 88.0±1.0 | 6.0±1.0 | 6.0 | 47±2 | 76 | 75±10 | 60 |
Reamrks:
(a) Solid content 20%, dissolved in MEK, Brookfield viscometer(25℃)
(a1)Solid content 20%, dissolved in MIBK/Toluene=1:1, Brookfield viscometer (25℃)
(b) Maleic acid
(c) Vinyl alcohol
Packing & storage:
1, 25kgs/ bag; 15000kgs /1x20’GP with pallet.
2, Stored in dry and ventilated conditions and at room temperature (about 25 ℃), avoiding direct sunlight.
Vinyl Copolymer resin for printing inks (screen & gravure)
Vinyl polymer resin
Specification:
1. Vinyl Copolymer resin (CAS NO.:9003-22-9)
It is a White powder, mainly use for Printing inks (screen & gravure),
Adhesive for PVC, heat-seal lacquer, Coating for leather & plastic etc.....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a) mPa.s | |
VC | VAC | ||||
VC50A | 85.0±1.0 | 15.0±1.0 | 52±1 | 75 | 43±10 |
VC55A | 87.0±1.0 | 13.0±1.0 | 55±1 | 76 | 52±10 |
VC62A | 87.0±1.0 | 13.0±1.0 | 62±1 | 76 | 75±10 |
VC68A | 87.0±1.0 | 13.0±1.0 | 68±1 | 76 | 90±20 |
2. Carboxyl Modified Vinyl Terpolymer Resin (CAS NO.:9005-09-8)
It is a White powder,mainly use for Screen printing ink, Gravure ink,
Adhesive for Aluminum foil heat-seal lacquer, Coating & Paint etc....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a) mPa.s | Acid value | ||
VC | VAc | Other(b) | |||||
VCVAM | 84.0±1.0 | 15±1.0 | 1.0 | 55±1 | 74 | 49±10 | 7.0±1.5 |
VCVAA | 85.0±1.0 | 14±1.0 | 1.0 | 61±1 | 75 | 65±10 | 7.0±1.5 |
VCVAB | 85.0±1.0 | 14±1.0 | 1.0 | 55±1 | 75 | 60±10 | 7.0±1.5 |
VCVAC | 84.0±1.0 | 14±1.0 | 2.0 | 55±1 | 73 | 60±10 | 14.0±2.0 |
3. Hydroxyl Modified Vinyl Terpolymer Resin (CAS NO.:25086-48-0)
Mainly use for PET Lamination ink, gravure & flexo printing ink,
Adhesive for tape& magnetic, Coating & Paint etc....
Models | Composition | Adhesion | Tg /℃ (DSC) | Viscosity (a1) mPa.s | Whiteness | ||
VC | VAc | Other(c) | |||||
VCOH | 88.0±1.0 | 6.0±1.0 | 6.0 | 61±2 | 76 | 240±20 | 60 |
VCH | 88.0±1.0 | 6.0±1.0 | 6.0 | 47±2 | 76 | 75±10 | 60 |
Reamrks:
(a) Solid content 20%, dissolved in MEK, Brookfield viscometer(25℃)
(a1)Solid content 20%, dissolved in MIBK/Toluene=1:1, Brookfield viscometer (25℃)
(b) Maleic acid
(c) Vinyl alcohol
Packing & storage:
1, 25kgs/ bag; 15000kgs /1x20’GP with pallet.
2, Stored in dry and ventilated conditions and at room temperature (about 25 ℃), avoiding direct sunlight.