Quantity: | |
---|---|
elite-indus
below 400g
720KGS by LCL
yes
Index | Standard(High purity) |
Color No. ( Fe-Co ) | ≤ 6 |
Acid value ( mgKOH / g ) | 190-205 |
Not soap compounds ( % ) | ------- |
Soap-based price ( mgKOH / g ) | ------- |
Dimer acid composition | =0.2 =95 =4.0 |
Monomer acid % Dimer acid % Trimer acid % | |
Viscosity ( mpa ּ S/25 ℃ ) | 6500-8500 |
Density ( g/cm325 ℃ ) | ------ |
Flash point (open) ℃ | ----- |
Index | Standard | ||||
ELT-116 | ELT-126 | ELT-136 | ELT-156 | ELT-166 | |
Color No. ( Fe-Co ) | ≤ 8 Iron cobalt colorimetric | ||||
Acid value ( mgKOH / g ) | 190 ± 5 | 190-198 | |||
Not soap compounds ( % ) | <1 | ----- | |||
Soap-based price ( mgKOH / g ) | ≥ 190 | 192-202 | |||
Dimer acid composition | <1 >85 <14 | 1-5 75-82 15-22 | 1-3 75-82 15-22 | 1-3 75-82 15-22 | 1-3 75-82 15-22 |
Monomer acid % Dimer acid % Trimer acid % | |||||
Viscosity ( mpa ּ S/25 ℃ ) | 6000 ~ 8500 | 5000~6000 | 6000~7000 | 7000~8000 | 8000~9000 |
Density ( g/cm325 ℃ ) | 0.932 ± 0.02 | ------ | |||
Flash point (open) ℃ | > 260 | ------ |
Index | Standard(High purity) |
Color No. ( Fe-Co ) | ≤ 6 |
Acid value ( mgKOH / g ) | 190-205 |
Not soap compounds ( % ) | ------- |
Soap-based price ( mgKOH / g ) | ------- |
Dimer acid composition | =0.2 =95 =4.0 |
Monomer acid % Dimer acid % Trimer acid % | |
Viscosity ( mpa ּ S/25 ℃ ) | 6500-8500 |
Density ( g/cm325 ℃ ) | ------ |
Flash point (open) ℃ | ----- |
Index | Standard | ||||
ELT-116 | ELT-126 | ELT-136 | ELT-156 | ELT-166 | |
Color No. ( Fe-Co ) | ≤ 8 Iron cobalt colorimetric | ||||
Acid value ( mgKOH / g ) | 190 ± 5 | 190-198 | |||
Not soap compounds ( % ) | <1 | ----- | |||
Soap-based price ( mgKOH / g ) | ≥ 190 | 192-202 | |||
Dimer acid composition | <1 >85 <14 | 1-5 75-82 15-22 | 1-3 75-82 15-22 | 1-3 75-82 15-22 | 1-3 75-82 15-22 |
Monomer acid % Dimer acid % Trimer acid % | |||||
Viscosity ( mpa ּ S/25 ℃ ) | 6000 ~ 8500 | 5000~6000 | 6000~7000 | 7000~8000 | 8000~9000 |
Density ( g/cm325 ℃ ) | 0.932 ± 0.02 | ------ | |||
Flash point (open) ℃ | > 260 | ------ |