Copolymer Polypropylene Macro Synthetic Fiber Twist hybrid

ELT-TWIST is a 100% virgin blended copolymer synthetic Structural macro-fiber successfully used as an alternate to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications.
Quantity:
  • ELT-TWIST

  • ELITE-INDUS

  • 5503400000

  • Copolymer Polypropylene

  • 500 to 800 Mpa

  • 5000Mpa

  • 0.3mm+/-0.05mm

  • 0.91+/-0.01 g/cm3

  • 160 - 170

  • 15+/-5%

  • Strong

  • White, Black, Gray,Natural

 
Macro Synthetic Fiber TWIST hybrid

Description 
ELT-TWIST is a 100% virgin blended copolymer synthetic Structural macro-fiber successfully used as an alternate to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications.

ELT-Twist is actually a Hybrid of two fibers: A standard fibrillated polypropylene fiber to reduce and control shrinkage and temperature cracking.
A twisted-bundle monofilament fiber made of a strong synthetic copolymer, to increase load-transfer and post-crack performance.


ELT-TWIST fibers comply with ASTM C1116, Standard Specification for Fiber Reinforced Concrete and Shotcrete, and are specifically used for the reduction of plastic shrinkage cracks, to improve impact, shatter and abrasion resistance, to increase fatigue resistance, to increase toughness of concrete and provide long term durability of concrete, structural enhancements and cement based building products.

Functions
· Increases impact, shatter and abrasion resistance of concrete
· Reduces segregation, plastic settlement, and shrinkage cracking of concrete
· Provides three-dimensional reinforcement against macro-cracking
· Increases overall durability, fatigue resistance and flexural toughness
· Reduction of in-place cost versus wire mesh for temperature / shrinkage crack control
· Easily added to concrete mixture at any time prior to placement

Application
· Industrial and residential floors
· Whitetoppings, bridge decks and pavements
· Thin walled pre-cast (septic tanks, vaults, walls, etc.)
· Mass concrete

Specification

Density(g/cm 3 ) 0.91 +/- 0.01 Equivalent Dia(mm) 0.3±0.05
Shape twist break tensile Ratio(%) 8-15
Crack Ratio (%) 20+/-5 Melting point ( C. Deg) 160-170
Tensile Strength (Mpa) 500 to 800 Water Absorption Negligible
Elastic Modulus (Mpa) >3500 Resistance to acid & alkali Excellent
Material Virgin Copolymer/Polypropylene
Length(mm) 38/48 /54 or as per your request
Dosage rates will vary depending upon the reinforcing requirements and can range from 2kg/m³ to 5 kg/m³
 
Directions for Use

ELT-TWIST fibers can be added to the concrete mixture at any time prior to placement of the concrete.
It is generally recommended to add any fiber material at the ready-mix concrete plant during batching.

Fibers must be mixed with concrete for a minimum of three to five minutes at maximum mixing speed, depending on the mixer type, to ensure complete dispersion and uniformity.

 
Packing

Shape Inner Packing(PE Film Bag) Outer Packing(Plastic Woven Bag) 20’gp 40’HQ
Twist 0.5/1.0kg 10kg 5500kg 12000kg
Inner Packing(Water Soluble Paper Bag) Outer Packing (Carton)
0.5/1.0kg 10kg 4000kg 9000kg
Other Packing Can As Per Your Request

Contact information:
Email: mika@elite-indus.com
Wechat/WhatsApp: 0086-15212447276
Previous: 
Next: 

CONTACT US

Add: 18F Tower C, Winning Ocean Plaza, No. 680 South Maanshan Road, Hefei, China
Tel: 0086-551-6237 2118       
Fax: 0086-551-6237 2117

SALES

Tel: 0086-551-6237 2126, 6237 2128
       E-mail: Jackhu@elite-indus.com
Complain & Suggestions: 
       Tel: 0086-551-6237 2125
       Email: admin@elite-indus.com

Anhui Elite Industrial Co.,ltd

Copyright © 2015,Anhui Elite Industrial Co.,ltd